We provide galvanization in weakly acidic and alkaline electrolyte. These electrolytes are in these days most popular technologies of galvanizing. They provide a high gloss surface with a thin and ductile layer.
GALVAN CZ s.r.o. performs galvanizing without passivation or with blue, thick-film or yellow passivation. All passivations are CrVI-free and are based on CrIII solutions. For all types of finishes we offer different kinds of sealings and top-coats.
Zinc plating is performed on a computer-controlled automatic lines with traceability of all parameters of the plating process.
RACK ZINC PLATING
Maximum dimensions of parts up to:
Line Z1 1800 mm x 300 mm x 1050 mm
Line Z3 2000 mm x 500 mm x 950 mm
BARREL ZINC PLATING
Barrel plating maximum capacity is 80 kg per one barrel.
Maximum dimensions of parts up to 150 mm and a weight of approximately 0.3 kg
Coating thickness
Standard thickness of zinc coating is 8-15 µm. We adjust thickness according to customer requirements, but only up to 35 µm.
Suitable materials
Iron, steel and cast iron products are suitable for galvanizing. The quality of the input material fundamentally affect the appearance of plated parts.
Zinc coating passivations
In order to improve the corrosion resistance the zinc layer is passivated with one of the Cr3+ passivations.
Thin-layer passivation Cr3+: (blue) 0.08-0.1 µm on zinc layer. It is used for parts that are less exposed to corrosion.
Thick-layer passivation Cr3+: (slightly iridescent appearance) 0.2-0.3 µm on zinc layer. Higher corrosion resistance comparable to yellow chromate. The advantage is that it doesn’t contain Cr6+, but it doesn’t have the self-repairable effect in case of passivation is eroded. It is used as a substitute for yellow chromate.
Yellow chromate Cr3+: (yellow, rainbow like appearance) 0.2-0.5 µm on the zinc layer. Higher corrosion resistance.
The organic and mineral organic sealing
To improve the corrosion resistance, sealing can be used as a next step of surface treatment. The sealer is applied in a 2-4 µm layer. If this sealer is applied on thin- or thick-layer passivation, after drying out, it creates a transparent organic film. This film increases not only the corrosion protection, but also abrasion resistance. On yellow chromated sealer coatings it suppresses iridescent appearance and gains uniform yellowish hue.
For surface treatment we use chemicals from suppliers Schlötter, Atotech, Coventya and Kiesow.
SPECIFICATION OF THE REQUIREMENTS FOR ZINC PLATING
Requirements for surface treatment are set out in the relevant ISO-DIN standards. GALVAN CZ s.r.o. performs metal surfacing according to global standards for automotive engineering or according to customer specifications.
PRICE
The price depends on used technology, area of processed parts, weight of one part, annual quantity and total volume of orders. For more information contact us: